Low Velocity Impact Damage Response of Carbon Fiber Reinforced Composites at Low Temperatures

Yıl 2019, Cilt: 8 Sayı: 3, 35 - 60, 31.12.2019

Öz

Carbon Fiber Reinforced Composite (CFRC) plates have been subjected to low energy impact tests at 22,5°C (with strain gauge mounted), 22,5°C, 0°C, -30°C and -60°C separately. CFU10T carbon is chosen as fiber material and CR80 epoxy resin as matrix. The samples have been prepared as 100 X 100 mm. width/length and 2 mm. (thickness), 8 layered respectively and have been orientated as quasi-isotropic. The plate samples have been prepared by hand layup method. Low velocity impact tests have been carried out by Weight Drop Impact Test Setup according to ASTM D7136. Critical response force-time, strain and damage response have been investigated. It has been observed that; as the temperature decreases, contact forces increase and contact time decreases. The laminate number and lay up orientation also affect the low impact energy behavior of plates. As the temperature decreases, impact strength of CFRP plates decreases. It has been experimentally observed and proved that low temperature decreases impact strength.

Destekleyen Kurum

no

Proje Numarası

no

Teşekkür

no

Kaynakça

  • REFERENCES:[1] Reinhart TJ, Clements LL. (1987). "Introduction to Composites, Engineered Materials Handbook" Volume 1: Composites. In: Dostal CyrilA et al., editors. ASM International; p27.
  • [2] Agarwall, B. D. and Broutman, L. J. (1980), Analysis and Performance of Fiber Composites.
  • [3] Stuart W.J, (2010), "Composite Materials Lay Up Lab Lecture Notes" Edmonds Community College.
  • [4] Belingardi, G., Vadori, R., (2002), "Low velocity impact tests of laminate glass-fiber-epoxy matrix composite material plates", Internal Journal of Impact Engineering, Vol.27; pp. 213-229. [5] Mirevski, T., Marshall, I.H., Thomson, R., (2006), "The influence of impacter shape on the damage to composite laminates", Journal of Composite Structures, Vol. 76; pp.116-122 .[6] Aslan Z., Karakuzu R., Okutan B., (2003), ”The response of laminated composite plates under low-velocity impact loading", Journal of Composite Structures, Vol.59; pp.119-127.
  • [7] Milli, F., Necib, B., (2001), "Impact behavior of cross-ply laminated composite plates under low velocities", Journal of Composite Structures, Vol.51; pp.237-¬244.
  • [8] Hoşur, M.V., Karim, M.R., Jeelani, S., 2003), "Experimental investigations on the response of stitched/unstitched woven S2-glass/SC15 epoxy composites under single and repeated low-velocity impact loading", Journal of Composite Structures, Vol.61; pp.89-102.
  • [9] Kara, M. (2006) ,"Dynamic Response Of Low Velocity Impact Composites”, Ms. S. Thesis, Selçuk University, Institute Of Science and Technology, Konya, Turkey.
  • [10] K., Cha, O, Kim, S., Yang, i., (2001), "Affects of temperature on impact damages in CFRP composite laminates", Journal of Composite Structures, Vol.32; pp.669-682.
  • [11] Ibekwe S.J., Mensah, P., F., Li, G., Pang, S., Stubblefield, M., (2007), "Impact and post impact response of laminated beams at low temperatures", Journal of Composite Structures, Vol.79; pp.12-17.
  • [12] Gomez del Rro, T., Zaera, R., Barbero, E., Navarro, C, (2005), "Damage in CFRP due to low velocity impact at low temperature", Composite Engineering, Vol.36: pp.41-50.
  • [13] Lal, K.M. (1982), “Prediction of residual tensile strength of transversely impacted composite laminates”, Structure Solid Mechanics, NASA CP-Vol. 2245, pp.97-111.
  • [14] Whittingham, B., Marshall, I. H., Mitrevski, T., and Jones, R. (2004). “The response of composite structures with pre-stress subject to low velocity impact damage”,Composite Structures, Vol.66, pp.685-698.
  • [15] Husseinzadeh, R., Shokrieh, M. M., and Lessard, L. (2006). “Damage behaviour of fiber reinforced composite plates subjected to drop weight impact”, Composite Science and Technology, Vol.66, pp.61-68.
  • [16] Amin S. K.., Reza B., Mohammad M., and Reza N.J. (2006). “The Role of Temperature on Impact Properties of Kevlar/fiberglass”, Composites Part B. Elsevier, Vol.37, pp.593-602.
  • [17] Jeremy G., Aaran J., Mohammod M. and James S. (2005), “Low Velocity Impact Combination Kevlar/ Carbon Fiber Sandwich Composites”, Composite Structures. Elsevier Composites, Vol.69, pp.396-406.
  • [18] ASTM D7136 (2005). “Standard Test Method for Measuring The Damage Resistance Of A Fiber-Reinforced Polymer Matrix Composite To A Drop Weight Impact Event”, American Society For Testing and Materials, USA.

Karbon Fiber Takviyeli Kompositlerin Düşük Sıcaklıklarda Düşük Hızdaki Darbe Dayanımı

Yıl 2019, Cilt: 8 Sayı: 3, 35 - 60, 31.12.2019

Öz

Karbon fiber takviyeli kompozitler (KFTK); 22,5°C (strain–gage li), 22,5°C, 0°C, -30°C ve-60°C sıcaklıklarda düşük enerjili darbe testlerine tabi tutulmuşlardır. CFU10T karbon fiber ve CR80 reçine matriks malzeme olarak kullanılmıştır. Numuneler 100 X 100 mm. genişlik/uzunluk ve 2 mm. kalınlıkta 8 tabakalı olarak hazırlanmış ve quasi-isotropic olarak ayrı ayrı yönlendirilmişlerdir. Tabakalar el yapımı yayma metodu ile hazırlandıktan sonra ASTM D7136’ya göre düşük hızda darbe testine tabii tutulmuşlardır. Kritik kuvvet-zaman, gerinim-zaman grafikleri hazırlanarak ayrı ayrı hasar analizleri yapılmıştır. Sıcaklık azaldıkça temas kuvvetinin arttığı ve temas zamanının azaldığı gözlemlenmiştir.

Proje Numarası

no

Kaynakça

  • REFERENCES:[1] Reinhart TJ, Clements LL. (1987). "Introduction to Composites, Engineered Materials Handbook" Volume 1: Composites. In: Dostal CyrilA et al., editors. ASM International; p27.
  • [2] Agarwall, B. D. and Broutman, L. J. (1980), Analysis and Performance of Fiber Composites.
  • [3] Stuart W.J, (2010), "Composite Materials Lay Up Lab Lecture Notes" Edmonds Community College.
  • [4] Belingardi, G., Vadori, R., (2002), "Low velocity impact tests of laminate glass-fiber-epoxy matrix composite material plates", Internal Journal of Impact Engineering, Vol.27; pp. 213-229. [5] Mirevski, T., Marshall, I.H., Thomson, R., (2006), "The influence of impacter shape on the damage to composite laminates", Journal of Composite Structures, Vol. 76; pp.116-122 .[6] Aslan Z., Karakuzu R., Okutan B., (2003), ”The response of laminated composite plates under low-velocity impact loading", Journal of Composite Structures, Vol.59; pp.119-127.
  • [7] Milli, F., Necib, B., (2001), "Impact behavior of cross-ply laminated composite plates under low velocities", Journal of Composite Structures, Vol.51; pp.237-¬244.
  • [8] Hoşur, M.V., Karim, M.R., Jeelani, S., 2003), "Experimental investigations on the response of stitched/unstitched woven S2-glass/SC15 epoxy composites under single and repeated low-velocity impact loading", Journal of Composite Structures, Vol.61; pp.89-102.
  • [9] Kara, M. (2006) ,"Dynamic Response Of Low Velocity Impact Composites”, Ms. S. Thesis, Selçuk University, Institute Of Science and Technology, Konya, Turkey.
  • [10] K., Cha, O, Kim, S., Yang, i., (2001), "Affects of temperature on impact damages in CFRP composite laminates", Journal of Composite Structures, Vol.32; pp.669-682.
  • [11] Ibekwe S.J., Mensah, P., F., Li, G., Pang, S., Stubblefield, M., (2007), "Impact and post impact response of laminated beams at low temperatures", Journal of Composite Structures, Vol.79; pp.12-17.
  • [12] Gomez del Rro, T., Zaera, R., Barbero, E., Navarro, C, (2005), "Damage in CFRP due to low velocity impact at low temperature", Composite Engineering, Vol.36: pp.41-50.
  • [13] Lal, K.M. (1982), “Prediction of residual tensile strength of transversely impacted composite laminates”, Structure Solid Mechanics, NASA CP-Vol. 2245, pp.97-111.
  • [14] Whittingham, B., Marshall, I. H., Mitrevski, T., and Jones, R. (2004). “The response of composite structures with pre-stress subject to low velocity impact damage”,Composite Structures, Vol.66, pp.685-698.
  • [15] Husseinzadeh, R., Shokrieh, M. M., and Lessard, L. (2006). “Damage behaviour of fiber reinforced composite plates subjected to drop weight impact”, Composite Science and Technology, Vol.66, pp.61-68.
  • [16] Amin S. K.., Reza B., Mohammad M., and Reza N.J. (2006). “The Role of Temperature on Impact Properties of Kevlar/fiberglass”, Composites Part B. Elsevier, Vol.37, pp.593-602.
  • [17] Jeremy G., Aaran J., Mohammod M. and James S. (2005), “Low Velocity Impact Combination Kevlar/ Carbon Fiber Sandwich Composites”, Composite Structures. Elsevier Composites, Vol.69, pp.396-406.
  • [18] ASTM D7136 (2005). “Standard Test Method for Measuring The Damage Resistance Of A Fiber-Reinforced Polymer Matrix Composite To A Drop Weight Impact Event”, American Society For Testing and Materials, USA.
Toplam 16 adet kaynakça vardır.

Ayrıntılar

Birincil Dil İngilizce
Konular Makine Mühendisliği
Bölüm Araştırma Makaleleri
Yazarlar

Zafer Özdemir 0000-0002-7919-5642

Selim Türkbas 0000-0002-9262-8844

Dilara Yılmaz

Proje Numarası no
Yayımlanma Tarihi 31 Aralık 2019
Gönderilme Tarihi 9 Ekim 2019
Yayımlandığı Sayı Yıl 2019 Cilt: 8 Sayı: 3

Kaynak Göster

IEEE Z. Özdemir, S. Türkbas, ve D. Yılmaz, “Low Velocity Impact Damage Response of Carbon Fiber Reinforced Composites at Low Temperatures”, DÜFED, c. 8, sy. 3, ss. 35–60, 2019.


DUFED is indexed/abstracted/enlisted in

Google Scholar | CABI - CAB Abstracts and Global Health | CAS Chemical Abstracts Service | ROAD Directory of Open Access Scholarly Resources | Index Copernicus | CiteFactor Academic Scientific Journals | BASE Bielefeld Academic Search Engine | Open AIRE | IJIFACTOR | ASOS Index | Paperity Open Science Aggregated | I2OR International Institute of Organized Research | SJIF Scientific Journal Impact Factor | Advanced Science Index | DRJI Directory of Research Journals Indexing | SOBİAD | AcarIndex | SIS Scientific Indexing Services | Crossref | Harman Türkiye Akademik Arşivi | AccessOn | Dimensions | Wizdom | OUCI The Open Ukrainian Citation Index | WorldCat | Scilit | ASCI Asian Science Citation Index

  cc.logo.large.png       Creative Commons License

28576
DUFED is a diamond open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles, or use them for any other lawful purpose, without asking prior permission from the publisher or the author. This is in accordance with the BOAI definition of open access. In addition, authors are not charged article processing fees or publication fees - no fees whatsoever. Importantly, authors retain the copyright of their work and allow it to be shared and reused, provided that it is correctly cited.

1024px-DOI_logo.svg.png https://doi.org/10.55007/dufed.xxxxxxx